偏铝酸锂

偏铝酸锂
	IUPAC名; Lithium aluminate
	系统名; Lithium(1+) aluminate
别名	铝酸锂
识别
CAS号	12003-67-7
PubChem	123268
ChemSpider	109880
SMILES	[Li+].[O-][Al]=O;
InChI	1/Al.Li.2O/q;+1;;-1/rAlO2.Li/c2-1-3;/q-1;+1;
InChIKey	YQNQTEBHHUSESQ-YICCBGQXAE
EINECS	234-434-9
MeSH	Lithium+aluminate
性质
化学式	AlLiO2
摩尔质量	65.92 g·mol−1
外观	白色晶体
密度	2.615 g/cm3（固体）
熔点	1625 °C（1898 K）
溶解性（水）	难溶
热力学
ΔfHm⦵298K	-1188.670 kJ/mol
S⦵298K	53.35 J/mol·K
	若非注明，所有数据均出自标准状态（25 ℃，100 kPa）下。

偏铝酸锂是一种无机化合物，化学式为LiAlO₂，是锂的铝酸盐之一。

制备

早期方法

偏铝酸锂粉末的制备是基于Al
2O
3和含锂化合物如Li
2CO
3、LiOH、Li
2O、LiAc等的固相反应，反应温度为400 - 1000℃。由于锂在高温下的挥发与来自研磨设备的污染，一定粒径的纯净的偏铝酸锂难以合成。^[2]

现代方法

偏铝酸锂有多种方法可以合成，如湿法、溶胶-凝胶法、模板剂法、前驱体法、燃烧法等。固相法制得的产物是α-LiAlO
2；湿法主要则会得到两相——α-LiAlO
2和γ-LiAlO
2。^[3]六方结构的α-LiAlO₂（低温相）在修饰后会得到高温相的γ-LiAlO₂，有着四方晶系的结构（约900℃）。介稳的的β相有着单斜晶胞，它在900℃会转化为γ相。^[2]

参考文献

^ ^1.0 ^1.1 R. Robie, B. Hemingway, and J. Fisher, “Thermodynamic Properties of Minerals and Related Substances at 298.15K and 1bar Pressure and at Higher Temperatures,” US Geol. Surv., vol. 1452, 1978.
^ ^2.0 ^2.1 Chatterjee & Naskar “Novel technique for the synthesis of lithium aluminate (LiAlO2) powders from water-based sols” Journal of Materials Science Letters, Vol 22, Issue 24, pp 1747-1749
^ Synthesis of lithium aluminate by thermal decomposition of a lithium dawsonite-type precursor J. Jimenez-Becerril & I. Garcia-Sosa, Journal of Ceramic Processing Research. Vol. 12, No. 1, pp. 52-56 (2011)

[usgs-1] 1.0 ^1.1 R. Robie, B. Hemingway, and J. Fisher, “Thermodynamic Properties of Minerals and Related Substances at 298.15K and 1bar Pressure and at Higher Temperatures,” US Geol. Surv., vol. 1452, 1978.

[#1-2] 2.0 ^2.1 Chatterjee & Naskar “Novel technique for the synthesis of lithium aluminate (LiAlO2) powders from water-based sols” Journal of Materials Science Letters, Vol 22, Issue 24, pp 1747-1749

[3] Synthesis of lithium aluminate by thermal decomposition of a lithium dawsonite-type precursor J. Jimenez-Becerril & I. Garcia-Sosa, Journal of Ceramic Processing Research. Vol. 12, No. 1, pp. 52-56 (2011)

[1]

[2]

[3]